Default Cracked Block

After changing a leaking and worn out water pump I noticed a wet spot under the water pump. Looks like the engine block has been let freeze at some point and cracked about a 3 inch long crack. It just seeps like you see around the head gaskets on some A engines but I'm sure will be a problem when I finally get on the road for any distance. Since I don't know if the engine is a worn out junker yet I've decided to try and JB Weld the crack. I figure since there is no pressure and I prep this correctly it should work and if it doesn't I can always go the distance and have it brazed or lock-stitched.

I've drained the coolant and removed the radiator so I could get to the crack. I've used a dremel to V the crack and expose clean metal around so the epoxy has something to stick to. I will drill at each end to stop further cracking. Should I tap those holes and put screws in? I've found another product similar to JB Weld and they even have a video on repairing an engine block. https://m.youtube.com/watch?v=y-AT8f9J4_E


I read I believe a member here who said they have done this but used a vacuum and super glue before the JB Weld. Sounds reasonable to me and like a good idea but I don't know if there are any chemical reactions of the glue, antifreeze and the JB Weld?

I know some of you will say don't try this and I get that but I'm not willing to throw much capitol at this at the moment. I think I'm going to go for it and if it works or fails I'll post about it. You can point and say I told you so then. I believe it's all in the preparation but we will see.

Opinions anyway ????
History is offline   Reply With Quote
Old 11-09-2019, 11:07 AM   #2
Kurt in NJ
Senior Member
 
Kurt in NJ's Avatar
 
Join Date: May 2010
Location: on the Littlefield
Posts: 6,140
Default Re: Cracked Block

smear it with epoxy, maby in 5-10years you will have to do it again
Kurt in NJ is offline   Reply With Quote
Sponsored Links (Register now to hide all advertisements)
Old 11-09-2019, 11:51 AM   #3
eagle
Senior Member
 
eagle's Avatar
 
Join Date: Aug 2011
Location: Eagle Bend, MN
Posts: 2,025
Default Re: Cracked Block

I did it on a Model T head with a nasty crack. Worked great. After it was well cured I refilled it, then when that was well cured I filed and sanded it smooth, then paint. Never leaked, couldn't tell there had ever been a crack. You may want to carefully inspect the rest of the block, frost cracks often times show up along the side of the engine. I used the original JB weld, the quick type doesn't seem quite as good. make sure you do a good job of mixing it. Sounds like your prep is good.
__________________
"There are some that can destroy an anvil with a teaspoon and shouldn't be allowed to touch anything resembling a tool."
eagle is offline   Reply With Quote
Old 11-09-2019, 03:21 PM   #4
Neil Wilson
Senior Member
 
Neil Wilson's Avatar
 
Join Date: May 2010
Location: Boulder, CO
Posts: 559
Default Re: Cracked Block

Quote:
Originally Posted by Kurt in NJ View Post
smear it with epoxy, maby in 5-10years you will have to do it again
Kurt, Does "epoxy" mean JB Weld or something else?
__________________
[email protected] - email contact

https://aafords.com Ford Model AA Truck Club @ aafords.com
Neil Wilson is offline   Reply With Quote
Old 11-09-2019, 03:25 PM   #5
hotrodart
Senior Member
 
hotrodart's Avatar
 
Join Date: May 2010
Location: Shenandoah Valley Virginia
Posts: 220
Default Re: Cracked Block

JB Weld was developed for the Army specifically for fixing cracked cast iron engines. It's been used for this purpose on millions of engines with very good success.
hotrodart is offline   Reply With Quote
Old 11-09-2019, 03:38 PM   #6
Werner
Senior Member
 
Werner's Avatar
 
Join Date: Jan 2019
Location: Germany, near Aachen
Posts: 1,151
Default Re: Cracked Block

Sponsored Links (Register now to hide all advertisements)
My car is gradually losing the joy that I had. I'm going from one repair to the next. And that for a 35,000 "Top Show Car". In this year I spent almost 4000 for spare parts.

My big frustration is that today I wanted to replace the valve cover after the timing gear renewed and see that suddenly cooling water in the valve chamber is high. Where the fine crack comes from is unclear.

Comparable unfortunately with the theme starter.
Attached Images
File Type: jpg P1010228.jpg (81.4 KB, 341 views)
File Type: jpg P1010222KR.jpg (89.3 KB, 360 views)
__________________
Beste Gruesse aus Deutschland,
Werner


Ford Model A, Roadster, 1928
Citroen 11 CV, 1947
Hercules W 2000, 1976; (with NSU-Wankel Rotary Engine), Canadian version
Werner is offline   Reply With Quote
Old 11-09-2019, 03:55 PM   #7
Werner
Senior Member
 
Werner's Avatar
 
Join Date: Jan 2019
Location: Germany, near Aachen
Posts: 1,151
Default Re: Cracked Block

Quote:
Originally Posted by History View Post
... but I don't know if there are any chemical reactions of the glue, antifreeze and the JB Weld?.

Opinions anyway ????
History, guten Abend you depressed suffering comrade!

I've made the experience that epoxy resins are very resistant to engine oil, but not against antyfreese (Glysantin). Because these are polyglycols that dissolve plastics.

The compromise solution would be to use only water with corrosion protection and drain it in winter.


I try it.
__________________
Beste Gruesse aus Deutschland,
Werner


Ford Model A, Roadster, 1928
Citroen 11 CV, 1947
Hercules W 2000, 1976; (with NSU-Wankel Rotary Engine), Canadian version
Werner is offline   Reply With Quote
Old 11-10-2019, 01:24 AM   #8
Pete
Senior Member
 
Pete's Avatar
 
Join Date: May 2010
Location: Wa.
Posts: 5,374
Default Re: Cracked Block

Rest assured, if nothing else works, it can be saved by TIG welding.
Pete is online now   Reply With Quote
Old 11-10-2019, 02:56 AM   #9
dumb person
Senior Member
 
dumb person's Avatar
 
Join Date: Apr 2011
Location: South pacific island
Posts: 1,724
Default Re: Cracked Block

Yes you can drill the ends of the crack and push soft wire into the holes & 'peen' it in place with a tiny hammer. Or tap and screw small machine screws in it. Don't drive them in too hard.

I've always wanted to try making a dovetail style cut in the cracks of a water jacket and put tiny holes either side, and solder in some white metal. Never have & hope i never have to.

This video, rough, but it worked well.
https://www.youtube.com/watch?v=Er0BZVfzyqk
__________________
<Link> This is how we roll<Link>

"I'm Convinced that no one really reads posts anymore; they just fabricate what they think the post says then ramble on about red herrings."--Bob
Outcasts rules of old cars
#1 Fun is imperative, mainstream is overrated
#2 If they think it is impossible, prove them wrong
#3 If the science says it impossible you are not being creative enough.
#4 No shame in recreating something you never had
#5 If it were not for the law & physics you would be unstoppable
dumb person is offline   Reply With Quote
Old 11-10-2019, 09:50 AM   #10
J and M Machine
Senior Member
 
Join Date: Oct 2010
Location: 40 Mt.Vickery Rd. Southborough,MA 508-460-0733
Posts: 352
Default Re: Cracked Block

History:
That's a common place for it to crack from ice damage, I would also look on drivers side of block as well. It can be fixed permenantly through metal stitching.
https://www.jandm-machine.com/metalStitching.html
Attached Images
File Type: jpg IMG_1951.JPG (55.2 KB, 237 views)
File Type: jpg IMG_1998.JPG (43.1 KB, 242 views)
J and M Machine is offline   Reply With Quote
Old 11-10-2019, 09:55 AM   #11
J and M Machine
Senior Member
 
Join Date: Oct 2010
Location: 40 Mt.Vickery Rd. Southborough,MA 508-460-0733
Posts: 352
Default Re: Cracked Block

Hello Werner:
That is stress crack we see often , It also can be repaired by metal stitching.
Attached Images
File Type: jpg IMG_4296.JPG (50.2 KB, 241 views)
File Type: jpg IMG_4389.JPG (54.2 KB, 218 views)
J and M Machine is offline   Reply With Quote
Old 11-10-2019, 03:32 PM   #12
Werner
Senior Member
 
Werner's Avatar
 
Join Date: Jan 2019
Location: Germany, near Aachen
Posts: 1,151
Default Re: Cracked Block

Good evening together,

I'm unlucky! After sanding the crack in the engine block today, I've seen that it's more than 4 inches long. From the back in the 90° bend to the front to the outlet channel.

Therefore JB Weld can not help, because the crack runs between the two outlet holes and gets very hot.

I am at a loss as to whether this can be welded. "Stichin '" - I've looked at -, that I not useable because of the unfavorable surface curvature.
Attached Images
File Type: jpg P1010254.jpg (76.8 KB, 261 views)
File Type: jpg P1010262.jpg (68.8 KB, 238 views)
__________________
Beste Gruesse aus Deutschland,
Werner


Ford Model A, Roadster, 1928
Citroen 11 CV, 1947
Hercules W 2000, 1976; (with NSU-Wankel Rotary Engine), Canadian version
Werner is offline   Reply With Quote
Old 11-10-2019, 04:42 PM   #13
mike657894
Senior Member
 
mike657894's Avatar
 
Join Date: Oct 2015
Location: Bay City Michigan
Posts: 1,050
Default Re: Cracked Block

This guy migs a cast iron pan. I havent tried this yet but will next time https://www.youtube.com/watch?v=JS8OLJ07emg
mike657894 is offline   Reply With Quote
Old 11-10-2019, 04:56 PM   #14
fastroadster
Senior Member
 
Join Date: Oct 2014
Location: Santa Cruz Ca.
Posts: 175
Default Re: Cracked Block

In the old days, we used "Water Glass". Sodium Silicate, you can buy it at a pharmacy. It was an egg preservative. You start up the A, let it warm up good. Then put 4oz of water glass in radiator. Put cap on and drive it. What happens is once the water glass hits air (crack) it hardens up. Been using it on old cars and tractors for years. Sounds Hoaky, but it works......
fastroadster is offline   Reply With Quote
Old 11-10-2019, 07:22 PM   #15
1928Mustang
Junior Member
 
Join Date: Mar 2019
Posts: 17
Default Re: Cracked Block

What rod do you use to tig weld cast iron?
1928Mustang is offline   Reply With Quote
Old 11-10-2019, 08:19 PM   #16
Pete
Senior Member
 
Pete's Avatar
 
Join Date: May 2010
Location: Wa.
Posts: 5,374
Default Re: Cracked Block

Quote:
Originally Posted by 1928Mustang View Post
What rod do you use to tig weld cast iron?
ER70.
If you need more info, email me.
Pete is online now   Reply With Quote
Old 11-11-2019, 02:35 PM   #17
Werner
Senior Member
 
Werner's Avatar
 
Join Date: Jan 2019
Location: Germany, near Aachen
Posts: 1,151
Default Re: Cracked Block

Hallo and good evening,



in my engine block, the now 5 inch long crack is very deep too into the material. I try to weld this into a special TIG company. Maybe with success.

Does anyone know what that iron ore cast material it was at the building time?



And, by the way: Is there something important, which has to be considered before I lift the engine?



I thank you in advance!
__________________
Beste Gruesse aus Deutschland,
Werner


Ford Model A, Roadster, 1928
Citroen 11 CV, 1947
Hercules W 2000, 1976; (with NSU-Wankel Rotary Engine), Canadian version
Werner is offline   Reply With Quote
Old 11-11-2019, 03:50 PM   #18
captndan
Senior Member
 
captndan's Avatar
 
Join Date: Nov 2015
Location: Tennessee
Posts: 714
Default Re: Cracked Block

A (good) welder can fix that crack. Amateurs usually cannot.
captndan is offline   Reply With Quote
Old 11-11-2019, 08:56 PM   #19
richard crow
Senior Member
 
Join Date: May 2010
Posts: 1,763
Default Re: Cracked Block

at the ends of the crack drill a small hole then hammer in a piece of sorda now get a can of zotight follow instructions your problem is over
richard crow is offline   Reply With Quote
Old 11-12-2019, 01:45 AM   #20
Werner
Senior Member
 
Werner's Avatar
 
Join Date: Jan 2019
Location: Germany, near Aachen
Posts: 1,151
Default Re: Cracked Block

Good moning Richard,


please tell me, what is "sorda", what is "zotight"?


Thanks.
__________________
Beste Gruesse aus Deutschland,
Werner


Ford Model A, Roadster, 1928
Citroen 11 CV, 1947
Hercules W 2000, 1976; (with NSU-Wankel Rotary Engine), Canadian version
Werner is offline   Reply With Quote
Reply

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

Sponsored Links (Register now to hide all advertisements)


All times are GMT -5. The time now is 12:29 PM.