[jrelliott]

If you do use Oak, use the white oak if possible. If you must use red oak make sure to preserve it with a good preservative like oil based spar varnish. You do not want moisture getting to it as will turn black especially where it meets the iron. Like other have stated, Ash will bend a lot more than oak and will not explode when bent like oak as it is more stringy.